eSUN eResin-Flex 0.5kg for 3d printer resin Flexible resin 405nm 3d printing lcd printer


Color: yellow
Prix:
Prix réduit$36.00

Description

eSUN eResin-Flex
Founded in 2002, Shenzhen eSUN Industrial Co., Ltd. is a national high-tech enterprise, a national strategic emerging industry new material project undertaker, and one of China's top ten biodegradable enterprises.
Product features:
[Resin]
Similar to TPU flexibility. High flexibility. High elasticity. Hardness 85-90A. High hardness. Abrasion resistance. Tear strength. Good resistance. Flexibility, elasticity, and compression. Designed specifically for LED light sources. "High Precision and Low Shrinkage" ESUN flexible resin contains polyurethane acrylate monomers to reduce volume shrinkage during the copying process, ensuring high accuracy and good finish of the printing model.
[Excellent fluidity and high stability]
The fast UV resin ensures the strength of the casting without excessive shrinkage, but also improves the printing speed, shortens the curing time, and improves the printing efficiency of the liquid crystal display machine. "Professional liquid crystal molding resin" uses high-quality pigments and photo initiators, and the pure color of the printing pattern is impressive. Compatible with most 3D LCD printers for rapid prototyping, including toy, artwork, and crafts, household tools, or jewelry manufacturing.
[Safety packaging]
Net weight: 500g. Fully shielded thickened aluminum bottle. Leak proof bottles completely wrapped with foam plastic bags to ensure that the resin remains where it belongs.
 3D PRINTING PHOTOPOLYMER RESIN Properties Table
3D PRINTING PHOTOPOLYMER RESIN eResin-Flex
Viscosity(mPa·s) 600-1400
Density(g/cm3) 1.02-1.05
Tensile Strength(MPa) 4-10
Elongation at Break(%) 100-350
Flexural Strength(MPa) /
Impact Strength(J/m) /
Tearing Strength(GPa) 8-30
Heat Distortion Temp(℃) /
Hardness(Shore D)  60-90A
Grades (out of 10)
Strength(S)  2
Toughness(F)  10
Forming(P)  4
Accuracy(S)  6
Speed (A)  4

 